ABSTRACT
In the present paper, the analysis of SEM and EDS results of porous and enriched in calcium, magnesium, zinc, copper and phosphorus coatings, obtained during 3-minute treatments performed by Plasma Electrolytic Oxidation (PEO)/Micro Arc Oxidation (MAO) processes on CP Titanium Grade 2, is presented. The PEO process was carried out at DC potentials of 500 VDC, 575 VDC, and 650 VDC in electrolytes containing 125 g Ca(NO3)2·4H2O, and 125 g Mg(NO3)2∙6H2O, and 125 g Zn(NO3)2∙6H2O, and 125 g Cu(NO3)2∙3H2O in 1 L H3PO4. It was found that obtained coatings have pores with different shapes and diameters and/or size/dimentions. The Ca/P, Mg/P, Zn/P, Cu/P, and M/P ratios (M=Ca+Mg+Zn+Cu) were equal to 0.074, 0.046, 0.056, 0.042, and 0.218, respectively. The highest value of each of these ratios was recorded for 650 VDC. It may be concluded that the obtained PEO coatings structures most likely are similar to hydroxyapatite-like structures, in which the Ca2+ may be replaced with Zn2+, Mg2+, Cu2+.
Support the magazine and subscribe to the content
This is premium stuff. Subscribe to read the entire article.